NHTSA Complaint #11677793 — 2006 TOYOTA TUNDRA

The frame on my 2006 Toyota Tundra SR5 has severe corrosion and multiple areas of rust perforation despite being treated under Toyota’s Limited Service Campaign D0D in 2015. During that campaign, the dealer removed the bed, documented active rust on the frame, cleaned it, and applied Corrosion-Resistant Compound (CRC) to key areas as the preventative remedy. As documented in multiple repairs the corrosion was already advancing at the time the CRC was applied, the steering shaft boot was replaced the same day as the compound was put on at 93,822 miles, several other critical safety failure shortly after; the brake pivots seized at 94900, Rotors rust pitted at 99537, bumper had perforations at 109407, 1 brake line from master cylinder and 1 brake line from ABS actuator leaking near the junction block on L/S of the frame at 113422, 52 days later the shift cable was broken at 114904. The current perforation and delamination indicate that the D0D remedy failed to prevent structural degradation as intended. The vehicle is available for inspection upon request. The vehicle’s structural integrity is severely compromised, creating a risk of frame failure while driving. This puts my safety and the safety of others at risk due to potential loss of control or component separation. The problem has not yet been inspected by the dealer in its current condition but has been escalated to Toyota Corporate. I have attached the communications with them. The truck has been fully serviced through Toyota since new, with the last documented service in January 2021. There were no warning lamps or dashboard messages prior to the failure. Visible rust first appeared prior to the D0D treatment and has now progressed to full perforation. The vehicle is currently unsafe to drive.